Fig. 3 is a TEM photograph of the microstructure of the weld bead, and it is understood that the base is a typical lath martensite. Since the lath martensite has a low carbon content, the substructure is a high-density dislocation and has a good overall performance, thereby contributing to improvement of weld toughness. The reason for obtaining low-carbon lath martensite in high-carbon welds is related to the early formation of large amounts of carbides. The content of Nb, Ti and V in the weld is high, and a large amount of uniform carbide is formed in the liquid droplet or molten pool to form a large amount of uniform carbide, so that the carbon content in the austenite matrix is ​​lowered, thereby avoiding the formation of brittle high carbon twin horse. Clan. On the other hand, the reduction of the carbon content of the matrix also reduces the precipitation of the network secondary carbide after the weld is solidified, and the splitting action on the substrate is alleviated.
image 3
Figure 4
b. Impact test and fracture observation
The weld no-notch impact test results are shown in Table 2, and the fracture morphology is shown in Figure 4. It can be seen from Table 2 and Figure 4 that the average impact toughness of the weld is 52 J/cm 2 , and the fracture is an obvious dimple-like fracture, indicating that the weld toughness is good.
Table 2 Impact toughness of weld specimen (αk, J/cm 2 )
Numbering | 1 | 2 | 3 | 4 | 5 |
Ä… k | 52 | 51 | 49 | 56 | 52 |
c. defect repair test
The surface defects of the 9Cr2Mo roll were trimmed with an angle grinder. After trimming, the defect size was about 30 mm and the depth was 8-10 mm. The cold welding process is used for defect repair. The interlayer temperature is about 35 ° C. Each layer is hammered immediately after welding to eliminate stress, so as to improve the grain morphology, eliminate the as-cast defects and reduce the welding stress. Magnetic particle inspection was performed after welding, and no cracks were found in the weld and heat affected zone. The weld hardness is 56-60HRC, which is close to the surface hardness of the 9Cr2Mo base metal (60-61HRC).
4 Conclusion
Surfacing test and test analysis shows that the use of strong carbide elements can obtain diffused carbonized material points in the cold-weld weld of tool steel, which can significantly improve the hardness and wear resistance of the weld; at the same time, the low carbon obtained in the weld The lath martensite matrix is ​​advantageous for improving the toughness and crack resistance of the weld. The new high-carbon Ti-Nb-V-Re-Cr alloy cold-weld weld can meet the requirements of cold-welding repair of tooling. The cold-welding process is simple and practical, and easy to promote.
Previous page
Beautiful: The back to wall Smart Toilet with hidden water tank design creates a clean and simple bathroom space. The absence of a visible tank gives the toilet a sleek, streamlined look that enhances the overall aesthetic of the space.
Easy to clean and maintain: With no exposed tank, cleaning the back-to-wall smart toilet just got easier. There are no nooks and crannies where dirt or dust can collect, making it easier to wipe and keep clean. Plus, the hidden tank is easily accessible when repairs or maintenance are required, saving time and effort.
Additional Features: The wall-mounted smart toilet is equipped with a range of advanced features for enhanced functionality and comfort. These may include self-cleaning systems, automatic deodorization, automatic flushing, bidet cleaning functions, and even night lights. These features provide additional comfort and convenience to the user.
Water efficiency and sustainability: Smart toilets feature water-saving technologies such as dual flush systems or high-efficiency flush mechanisms. This helps conserve water and promotes sustainable living. By reducing water usage, the back-to-wall smart toilet helps the environment.
In conclusion, the wall-mounted smart toilet has both aesthetic and functional advantages. Its hidden cistern design brings a clean, modern look to the bathroom, while also making cleaning and maintenance easier. Additional features enhance comfort and convenience, and a focus on water efficiency aligns with sustainable living practices. Overall, the wall-mounted smart toilet provides a comfortable, stylish and eco-friendly toileting experience.
Back To Wall Smart Toilet, Dual Flush Smart Toilet, Intelligent Water Closet, Hidden Cistern Toilet
Guangdong Fabia Intelligent Technology Co., Ltd , https://www.nbsmartfabiatoilet.com